  1.  Where strength is a design consideration, the alloys in the first column are
  2.  generally preferred over the more widely used alloys in the second column.
  3.  Note that the regular 0.08% carbon grades have somewhat higher strength than
  4.  the low carbon grades which are preferred for welded fabrication.
  5.  
  6.      304   in lieu of   304L            Pump and valve shafting
  7.  
  8.      321   in lieu of   304L            Industrial expansion joints
  9.  
  10.      347   in lieu of   304L            Aircraft expansion joints
  11.  
  12.      316   in lieu of   316L            Heat exchanger tubing
  13.                                         Pump and valve shafting
  14.  
  15.      329   in lieu of   316             Centrifuges
  16.  
  17.      301   in lieu of   304             Wheel covers
  18.  
  19.      201   in lieu of   304             Hose clamps, link belt chains